| Author: | Xu, Zibo |
| Title: | Iron speciation control on mineral-biochar composites for environment decontamination |
| Advisors: | Tsang, Dan (CEE) |
| Degree: | Ph.D. |
| Year: | 2023 |
| Subject: | Biochar Hazardous wastes Hazardous wastes -- Purification Hong Kong Polytechnic University -- Dissertations |
| Department: | Department of Civil and Environmental Engineering |
| Pages: | xv, 325 pages : color illustrations |
| Language: | English |
| Abstract: | Biochar, a carbon-rich material produced from the thermal treatment of biomass wastes with limited oxygen, was highlighted as a negative emission technology. Engineered biochar with a fit-for-purpose production can solve multiple environmental problems with the achievement of the circular economy. Among different modification technologies, impregnating iron (Fe) with the formation of Fe-biochar has been widely investigated owing to its high reactivity, natural abundance, facile synthesis, and environmental benignancy, while the precise control of Fe species on Fe-biochar for target pollutants immobilization is still unclear. This thesis focused on the precise control of Fe-species on Fe-biochar for the toxic metals immobilization process, and the key findings include: (i) Pyrolysis temperature affected the redox activity of the produced Fe-biochar. Increasing pyrolysis temperature altered the Fe-biochar from reductive to oxidative for the pollutants immobilization; (ii) The content of different carbon species in biochar led to distinct reductive-Fe and amorphous-Fe contents in the resulting Fe-biochar composites, and thus affected its immobilization mechanisms for arsenic; (iii) The crystallinity of Fe mineral affected the electron transfer routine with biochar during the Cr(VI) reduction process; (iv) Reductive transformation of Fe within the Fe-Mn binary oxide on Fe-Mn biochar was found during the pyrolysis process, forming embedded Fe(0) clusters within FeMnO2 with a high Fe efficiency for the Cr(VI) immobilization; and (v) The hydrothermal pretreatment affects the mineral species on the Fe-Mn biochar. Higher hydrothermal temperature with co-existing urea led to the formation of nano-sized Fe(0) surrounded by the lattice-expanded MnO and cotton-like graphitic carbon, providing a high immobilization capacity for the frequently-appeared toxic metals in electroplating water. Results from this study could serve as the guideline for efficient Fe-biochar production for toxic metal immobilization. Based on the current finding, future studies about particle size control, metal-carbon framework design, production standard of Fe-biochar, carbon emission of modified biochar, and overall economic concern are suggested to promote the engineered biochar for industrial-level application. |
| Rights: | All rights reserved |
| Access: | open access |
Copyright Undertaking
As a bona fide Library user, I declare that:
- I will abide by the rules and legal ordinances governing copyright regarding the use of the Database.
- I will use the Database for the purpose of my research or private study only and not for circulation or further reproduction or any other purpose.
- I agree to indemnify and hold the University harmless from and against any loss, damage, cost, liability or expenses arising from copyright infringement or unauthorized usage.
By downloading any item(s) listed above, you acknowledge that you have read and understood the copyright undertaking as stated above, and agree to be bound by all of its terms.
Please use this identifier to cite or link to this item:
https://theses.lib.polyu.edu.hk/handle/200/12543