| dc.title | Air plasma treatment of PDMS : surface physical properties and substrate for cell adhesion | en_US |
| dcterms.abstract | Polydimethylsibxane (PDMS) are widely used as supporting material for cell culturing in medical implants. However, current applications require PDMS to be biocompatibte for cell culturing and easy for processing. The aim of this project is to study the surface properties of PDMS after air plasma treatment and the effects of air plasma modified PDMS on cell adhesion. In this paper, the five groups are PDMS substrates modified by air plasma with different treated time (10s, 30s, 60s, 2min and 5min). Statistic contact angles are measured to evaluate the surface wettability properties change. Then, the treated surfaces are characterized using Scanning Electronic Microscopy (SEM) to observe the changes of surface morphology. Human esophageal squamous epithelial KYSE-30 cancer cells and rat bone marrow derived mesenchymal stem cells (MSC) were seeded onto untreated, treated and negative controlled samples. Cell density, cell morphology and viability were assessed at set time-points. As an effect of the air plasma treatment, the contact angles measured on PDMS surfaces decreased significantly. The treatment time had non-ignorable effect on the results. With increasing air plasma treated time, it has been observed that the PDMS surface has a much lower water contact angle as compared to the hydrophobic, native PDMS surface. Although air plasma treatment caused PDMS become hydrophilic, PDMS substrates could not retain this property over time. SEM analysis showed significant surface morphological changes between the 5min air plasma treated and untreated PDMS. The former surface has considerable cracks rather than untreated PDMS with relatively smooth surface. The data from in vitro assays showed that cell attachment onto negative control surface (TCPS) was significantly higher than those cultured on untreated and air plasma treated PDMS surfaces. However, the data also demonstrated that PDMS surfaces with longer time for air plasma treatment will support better adhesion and spreading for KYSE-30 cell lines than untreated PDMS surfaces. However, this phenomenon was not obvious between the 60s and 2min air plasma treated group which consistent with the result that the contact angles measured immediately after the air plasma treatment between 60s and 2min groups did not have significant difference. The fluorescein diacetate-propidium iodide staining method showed high cell viability on air plasma treated and untreated surfaces. The fluorescence microscopy results indicate that the cell morphology among the different air plasma treated groups and untreated PDMS surfaces were no distinct difference, however, the discrepancy observed from images in a high extent caused by the low observatbn resolution and the low cell density. For five groups with different air plasma treated time, both in the contact angle measurements and the cell adhesion evaluation, the treated effect was increased with the increased air plasma treated time. | en_US |
| dcterms.extent | xiii, 87 leaves : ill. (some col.) ; 30 cm. | en_US |
| dcterms.isPartOf | PolyU Electronic Theses | en_US |
| dcterms.issued | 2009 | en_US |
| dcterms.educationalLevel | All Master | en_US |
| dcterms.educationalLevel | M.Sc. | en_US |
| dcterms.LCSH | Hong Kong Polytechnic University -- Dissertations. | en_US |
| dcterms.LCSH | Cell culture -- Technique. | en_US |
| dcterms.LCSH | Cell adhesion. | en_US |
| dcterms.LCSH | Plasma engineering. | en_US |
| dcterms.LCSH | Surfaces (Physics) | en_US |
| dcterms.accessRights | restricted access | en_US |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| b23054955.pdf | For All Users (off-campus access for PolyU Staff & Students only) | 4.8 MB | Adobe PDF | View/Open |
Copyright Undertaking
As a bona fide Library user, I declare that:
- I will abide by the rules and legal ordinances governing copyright regarding the use of the Database.
- I will use the Database for the purpose of my research or private study only and not for circulation or further reproduction or any other purpose.
- I agree to indemnify and hold the University harmless from and against any loss, damage, cost, liability or expenses arising from copyright infringement or unauthorized usage.
By downloading any item(s) listed above, you acknowledge that you have read and understood the copyright undertaking as stated above, and agree to be bound by all of its terms.
Please use this identifier to cite or link to this item:
https://theses.lib.polyu.edu.hk/handle/200/5298