dc.titleDevelopment of calcium phosphate bioceramic composites for load-bearing applicationen_US
dcterms.abstractHydroxyapatite (HA) ceramic has attracted much attention due to its superior biocompatibility and bioactivity as a substitute material in bone grafting. HA has a superior bioactivity such that chemical bonding can be generated on the interface between HA implants and natural bones. However, its clinical applications are limited to free of high load-bearing situations due to its poor mechanical strength. In this project, nano-HA ceramic composites with improved mechanical strength and comparatively high bioactivity were fabricated for different load-bearing applications in bone tissue engineering. Nano-sized HA particles were synthesized in the first step to mimic HA in natural bone. A new synthesis method of nano-size needle-like HA particles was developed. Ultrasonic vibration was introduced in the co-precipitation synthesizing process, which provided more nucleation energy for the HA crystals, improved the nucleation density and consequently refined the HA crystals. Surfactant cetyltrimethyl-ammonium bromide (CTAB) was introduced in the fabricating process to improve dispersing properties and control the growing direction of nano-size HA crystals. Nano-size needle-like HA particles were fabricated with the aid of ultrasonic vibration and surfactant. Multi-wall carbon nanotubes (MWNTs) were chosen as the reinforcing phase to enhance the strength of nano-HA ceramics due to their unique mechanical properties and superior biocompatibility. In this study, the surfaces of MWNTs were modified to improve the dispersion property. An improved dispersion of the surface modified MWNTs in the HA matrix was achieved. The flexural strength and toughness of the fabricated nano-HA-MWNT composites with 7vol% MWNTs reached 103MPa and 1.28 MPa·m1/2, which were improvement about 34% and 51% compared with those of unmodified HA ceramics. HA-ZrO2-MWNT composites were designed and fabricated to further improve the mechanical strength of HA ceramics. The flexural strength and the toughness of the HA-ZrO2-MWNT composites reached 183 MPa and 2.20 MPa·m1/2 which were close to those of cortical bone (flexural strength: 50-150MPa, toughness: 2-12MPa·m1/2), when the volume percentages of the reinforcing phases of ZrO2 and MWNTs were 27vol% and 7vol%, respectively. The in-vitro method was used to test the bioactivity of the composites. The surfaces of the HA-MWNT samples were covered by a new growth layer after immersion for 3 days. The EDX results showed that the covered layer was calcium phosphate material. The results indicated that both HA-MWNT and HA-ZrO2-MWNT composites had comparatively high bioactivity. The mechanical and biological properties of the HA composites can be designed according to certain application requirements. Finite element models were constructed to study the reinforcing effects of MWNTs. In addition, a load bearing case for a dental implantation was also studied using the finite element method to explore the applicability of the HA composites. To conclude, nano HA composites with improved mechanical strength that can be used in load-bearing conditions were fabricated. The achievements of the present project can improve the quality of implants for hard tissue surgery in load bearing conditions. The new reinforcing method with multi-phase and multi-shape reinforcing phases can also be used as a reference in the design process for other composites.en_US
dcterms.extentxiii, 175 leaves : ill. ; 30 cm.en_US
dcterms.isPartOfPolyU Electronic Thesesen_US
dcterms.issued2010en_US
dcterms.educationalLevelAll Doctorateen_US
dcterms.educationalLevelPh.D.en_US
dcterms.LCSHHong Kong Polytechnic University -- Dissertationsen_US
dcterms.LCSHHydroxyapatite -- Biocompatibility.en_US
dcterms.LCSHBioactive compounds -- Biotechnology.en_US
dcterms.accessRightsopen accessen_US

Files in This Item:
File Description SizeFormat 
b23516999.pdfFor All Users6.15 MBAdobe PDFView/Open


Copyright Undertaking

As a bona fide Library user, I declare that:

  1. I will abide by the rules and legal ordinances governing copyright regarding the use of the Database.
  2. I will use the Database for the purpose of my research or private study only and not for circulation or further reproduction or any other purpose.
  3. I agree to indemnify and hold the University harmless from and against any loss, damage, cost, liability or expenses arising from copyright infringement or unauthorized usage.

By downloading any item(s) listed above, you acknowledge that you have read and understood the copyright undertaking as stated above, and agree to be bound by all of its terms.

Show simple item record

Please use this identifier to cite or link to this item: https://theses.lib.polyu.edu.hk/handle/200/5407