| dc.title | Large-area regular anodized alumina channel array fabrication assisted by nanoimprint lithography | en_US |
| dcterms.abstract | Porous anodic aluminium oxide (AAO) is a common template material for the preparation of nanoscale features. Highly regular pore arrays can be fabricated under specific conditions, but generally the range of regular pore alignment is only a few micrometers. Attempts have been made to improve the size of such domains of regular pore arrangements, in order to widen the application of the AAO templates. In this project, the conventional two-step anodization process was studied with an in-house setup. Anodization parameters were investigated to understand how they affect the pore growth process in both Al foils and Al thin films. Moreover, soft ultraviolet nanoimprint lithography was used to pattern Al sample surfaces, and the patterns were transferred into Al by physical etching. Subsequently, anodization was carried out. Patterns of triangular and square arrangements were used to demonstrate that both patterns can be used for guiding the growth of pores. Different dimensions of patterns were also used. With a matching anodization voltage, which is the voltage expected to form pores with a similar interpore distance as the patterned array lattice, pores grew at pre-defined locations. On the other hand, when pattern dimensions were larger than the interpore distance formed under the given anodization condition, multiple pores were formed within each imprinted hole, with no pores grown in unetched areas. Applications of the AAO have been demonstrated. Different types of materials have been deposited into the pores by different methods. The surface of AAO can also act as a substrate for surface-enhanced Raman scattering. | en_US |
| dcterms.extent | 112 leaves : ill. (some col.) ; 30 cm. | en_US |
| dcterms.isPartOf | PolyU Electronic Theses | en_US |
| dcterms.issued | 2012 | en_US |
| dcterms.educationalLevel | All Master | en_US |
| dcterms.educationalLevel | M.Phil. | en_US |
| dcterms.LCSH | Nanostructured materials. | en_US |
| dcterms.LCSH | Metals -- Anodic oxidation. | en_US |
| dcterms.LCSH | Aluminum oxide. | en_US |
| dcterms.LCSH | Nanotechnology. | en_US |
| dcterms.LCSH | Microlithography. | en_US |
| dcterms.LCSH | Hong Kong Polytechnic University -- Dissertations | en_US |
| dcterms.accessRights | open access | en_US |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| b25300921.pdf | For All Users | 49.57 MB | Adobe PDF | View/Open |
Copyright Undertaking
As a bona fide Library user, I declare that:
- I will abide by the rules and legal ordinances governing copyright regarding the use of the Database.
- I will use the Database for the purpose of my research or private study only and not for circulation or further reproduction or any other purpose.
- I agree to indemnify and hold the University harmless from and against any loss, damage, cost, liability or expenses arising from copyright infringement or unauthorized usage.
By downloading any item(s) listed above, you acknowledge that you have read and understood the copyright undertaking as stated above, and agree to be bound by all of its terms.
Please use this identifier to cite or link to this item:
https://theses.lib.polyu.edu.hk/handle/200/6704