| dc.title | Carbon-silicon nanocomposite anodes for energy storages | en_US |
| dcterms.abstract | Lithium ion batteries (LIBs) is a kind of newly emerging batteries with excellent properties of high energy density, high working voltage, high charging speed, long cycle life, safe and non-pollution which has already been widely used in recent years. Silicon is one of the most popular anode materials of Li-ion battery due to its high theoretical storage capacity. However, because of its poor electrical conductivity and dramatic capacity fading caused by the large volume expansion/contraction during the electrochemical reaction process, this material encounters great obstacles on the way to large-scale commercialization. In this thesis, two core-shell structures were prepared as reference objects. As carbon materials possess a better electrical conductivity and a more stable structure in the charge-discharge reaction, we used silicon nanoparticle-based composites, coating with a carbon layer to constrain the large volume expansion of silicon during the lithiation. The electrical analysis showed that, comparing with the pure silicon nanoparticles electrode, this structure could prevent the SEI films from continually forming, and improve the electrochemical performance to some extent. Besides carbon shell, a new TiO₂ layer was also studied to replace the carbon shell in the core-shell structure because the TiO₂ layer possesses a higher strength than carbon shell. And the electrochemical test result showed that the TiO₂ layer even did better in keeping the cycle stable. A novel yolk-shell structure was studied to improve the anode properties. It is a structure with a preexistent void between silicon nanoparticles and outer shell. In this thesis, carbon shell and TiO₂ shell were used to form the yolk-shell structure. With the TEM observation, the final composites had a yolk shell structure and the thickness of preexistent void and carbon shell were 50 nanometers and 15 nanometers, respectively while the thickness of preexistent void and TiO₂ shell were 50 nanometers and 30 nanometers. The optical microscope images demonstrated that this yolk-shell structure could efficiently eliminate the pulverization of electrode due to the silicon expansion. And electrical analysis also showed that the yolk-shell silicon nanocomposites electrode had a good electrochemical performance with high capacity, excellent rate capability, and cycle stability. | en_US |
| dcterms.extent | 118 pages : color illustrations | en_US |
| dcterms.isPartOf | PolyU Electronic Theses | en_US |
| dcterms.issued | 2017 | en_US |
| dcterms.educationalLevel | M.Sc. | en_US |
| dcterms.educationalLevel | All Master | en_US |
| dcterms.LCSH | Hong Kong Polytechnic University -- Dissertations | en_US |
| dcterms.LCSH | Energy storage | en_US |
| dcterms.LCSH | Lithium ion batteries -- Materials | en_US |
| dcterms.LCSH | Nanostructured materials | en_US |
| dcterms.accessRights | restricted access | en_US |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| 991021962224203411.pdf | For All Users (off-campus access for PolyU Staff & Students only) | 3.45 MB | Adobe PDF | View/Open |
Copyright Undertaking
As a bona fide Library user, I declare that:
- I will abide by the rules and legal ordinances governing copyright regarding the use of the Database.
- I will use the Database for the purpose of my research or private study only and not for circulation or further reproduction or any other purpose.
- I agree to indemnify and hold the University harmless from and against any loss, damage, cost, liability or expenses arising from copyright infringement or unauthorized usage.
By downloading any item(s) listed above, you acknowledge that you have read and understood the copyright undertaking as stated above, and agree to be bound by all of its terms.
Please use this identifier to cite or link to this item:
https://theses.lib.polyu.edu.hk/handle/200/9072