Full metadata record
DC FieldValueLanguage
dc.contributorDepartment of Electronic and Information Engineeringen_US
dc.contributor.advisorSurya, Charles (EIE)-
dc.creatorYu, Yang-
dc.publisherHong Kong Polytechnic University-
dc.rightsAll rights reserveden_US
dc.titleInvestigation on the WS₂ thin film growth and device fabricationen_US
dcterms.abstractTransition metal dichalcogenides (TMDC) layered materials with their remarkable layer-dependent electrical and optical properties have attracted a great deal of research interests recently. The weak van der Waals force dominated layer interactions can accommodate large lattice mismatch to reduce interface defects, because the bonds in a single layer are fully saturated. Additionally, lattice strain is almost absent between layers for such materials. These features make TMDC layered materials to be as potential materials for the fabrication of ultra-thin and flexible electronic and optoelectronic devices. Single-layer or few-layer TMDC materials can be easily acquired by mechanical exfoliation from a single crystal for basic investigations to fabricate proof-of-concept electronic devices. Nevertheless, the exfoliation method is limited to microscale, which is not appropriate for production on large scale. In this thesis, wafer-scale p-type WS2 thin film growth by molecular beam epitaxy (MBE) and chemical vapor deposition (CVD) had been systematically investigated. In addition, WS₂/GaN p-n junctions with low leakage current were fabricated by the transfer of p-type WS₂ thin films onto n-type GaN, and ultra-thin WS₂-based FETs were fabricated by using 40 nm WS₂ thin films as the channel layer. Only the (002) family X-ray diffraction (XRD) peaks were detected for the WS₂ thin film grown by MBE method, indicating strong preferential growth along the [001] crystal orientation of WS₂. For the CVD growth of the WS₂ thin film, by employing a thin Ni layer as texture promoter, the crystal structure of the WS₂ thin film changed from randomly oriented crystallites to large layered crystals with their c-axis oriented perpendicular to the growth substrate with the carrier mobility of 63.3 cm²/Vs. The liquid NiSx phase in the sulfurization process served as the liquid crystallization seeds for van der Waals rheotaxy resulting in horizontal growth of WS₂ crystallites with enhanced crystal size.en_US
dcterms.abstractTaking advantage of the hydrophobicity of WS₂ and hydrophilicity of sapphire substrates, the wafer-scale etching-free transfer method was developed to transfer the as-grown WS₂ thin films onto other substrates without inducing cracks or wrinkles to fabricate heterojunctions. Compared to conventional epitaxial-grown heterojunctions, a wide range of semiconductors can be used for the fabrication of heterojunctions by this etching-free transfer method. Additionally, the etching-free approach does not require the use of any destructive etchants and thereby enables the reuse of substrates. The p-n junctions fabricated by transferring p-type WS₂ thin films onto n-type GaN layer had a quite low leakage current density of 29.6 μA/cm², whereas the direct grown WS₂/GaN p-n junction had a large leakage current density of 92.4 mA/cm². This demonstrates superior performance of the transferred device compared to the as-grown WS2/GaN p-n junctions. This etching-free transfer method is expected to enormously expand the applications of WS₂ thin films for optoelectronic and electronic devices. Layered WS₂ thin films, which have fewer dangling bonds, are attractive for use as channel layers in ultra-thin field effect transistors (FETs). In this thesis, uniform large-area ultra-thin WS2 thin films, down to 40 nm, were obtained by a chemical etching method to fabricate ultra-thin FETs. The WS₂-based FET employing a 40 nm WS₂ thin film as the channel layer had a field-effect mobility of 0.54 cm2V-1s-1 and on/off ratio of 2700.en_US
dcterms.extentxvi, 187 pages : color illustrationsen_US
dcterms.isPartOfPolyU Electronic Thesesen_US
dcterms.educationalLevelAll Doctorateen_US
dcterms.LCSHHong Kong Polytechnic University -- Dissertationsen_US
dcterms.LCSHThin filmsen_US
dcterms.accessRightsopen accessen_US

Files in This Item:
File Description SizeFormat 
991022095454503411.pdfFor All Users9.59 MBAdobe PDFView/Open

Copyright Undertaking

As a bona fide Library user, I declare that:

  1. I will abide by the rules and legal ordinances governing copyright regarding the use of the Database.
  2. I will use the Database for the purpose of my research or private study only and not for circulation or further reproduction or any other purpose.
  3. I agree to indemnify and hold the University harmless from and against any loss, damage, cost, liability or expenses arising from copyright infringement or unauthorized usage.

By downloading any item(s) listed above, you acknowledge that you have read and understood the copyright undertaking as stated above, and agree to be bound by all of its terms.

Show simple item record

Please use this identifier to cite or link to this item: https://theses.lib.polyu.edu.hk/handle/200/9351