Full metadata record
| DC Field | Value | Language |
|---|---|---|
| dc.contributor | Department of Applied Physics | en_US |
| dc.contributor.advisor | Leung, C. W. (AP) | - |
| dc.creator | Ng, Sheung Mei | - |
| dc.identifier.uri | https://theses.lib.polyu.edu.hk/handle/200/9513 | - |
| dc.language | English | en_US |
| dc.publisher | Hong Kong Polytechnic University | - |
| dc.rights | All rights reserved | en_US |
| dc.title | Synthesis and characterization of tungsten disulphide | en_US |
| dcterms.abstract | Tungsten disulphide (WS₂) is a 2-dimensional layered material with each layer consisting S-W-S in strong covalent bond whereas weak van der Waals' force between layers. Weak bonding between layers allows the preparation of monolayers by mechanical exfoliation, which is the method firstly used for preparing graphene. However it is challenging to prepare large area flakes by such a method. Different techniques have been developed for the growth of WS₂ and novel properties at few-layer and monolayer were gradually discovered in recent years. In this project, two methods have been applied for the growth of WS₂. Direct sulphurization was applied on sputtered W films. It was found that WS₂ nanotubes were formed even at moderate temperatures. The crucial factor was the thickness of the precursor films. Ultrathin W films (0.5 and 0.7 nm) formed WS₂ nanotubes while thicker films showed nanoparticle-like surfaces. This morphology change was found to be stress-related. By patterning the films into micrometer-wide tracks, intrinsic stress in the ultrathin films was released and the critical loading stress for buckling was increased. The manipulation of WS₂ morphologies could be achieved simply by controlling the precursor films thickness or by conventional patterning technique. In addition, doping of WS₂ was studied by sulphurization of co-sputtered Ni-W films. Different doping concentrations were realized simply by controlling sputtering rates of Ni and W, which was confirmed by X-ray photoelectron spectroscopy (XPS) and energy dispersive X-ray spectroscopy (EDX). Structural and chemical analyses, including Raman spectroscopy, X-ray diffraction (XRD) and transmission electron microscopy (TEM) were performed. Electrical properties of the samples were also studied by measuring the resistance-temperature behaviour, confirming the semiconducting nature of pure and doped WS₂. Photodetectors were constructed from such WS₂ films. Doping with 5.1% Ni-WS₂showed the best photodetection performance among pure and heavily Ni-doped samples. Chemical vapour deposition (CVD), which allows the growth of single crystalline flakes by controlling the parameters involved in the reaction, was applied for the preparation of WS₂. The flakes were transferred to SiO₂/Si substrates. Electrical properties of WS₂ flakes were studied by constructing back-gate transistor. Spin Hall effect was preliminarily investigated by constructing Pt/WS₂/YIG tri-layer samples. | en_US |
| dcterms.extent | 112 pages : color illustrations | en_US |
| dcterms.isPartOf | PolyU Electronic Theses | en_US |
| dcterms.issued | 2018 | en_US |
| dcterms.educationalLevel | Ph.D. | en_US |
| dcterms.educationalLevel | All Doctorate | en_US |
| dcterms.LCSH | Hong Kong Polytechnic University -- Dissertations | en_US |
| dcterms.LCSH | Nanostructured materials | en_US |
| dcterms.LCSH | Graphene | en_US |
| dcterms.LCSH | Thin films | en_US |
| dcterms.accessRights | open access | en_US |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| 991022142059603411.pdf | For All Users | 6.53 MB | Adobe PDF | View/Open |
Copyright Undertaking
As a bona fide Library user, I declare that:
- I will abide by the rules and legal ordinances governing copyright regarding the use of the Database.
- I will use the Database for the purpose of my research or private study only and not for circulation or further reproduction or any other purpose.
- I agree to indemnify and hold the University harmless from and against any loss, damage, cost, liability or expenses arising from copyright infringement or unauthorized usage.
By downloading any item(s) listed above, you acknowledge that you have read and understood the copyright undertaking as stated above, and agree to be bound by all of its terms.
Please use this identifier to cite or link to this item:
https://theses.lib.polyu.edu.hk/handle/200/9513