| Author: | Zhu, Yinggang |
| Title: | Ammonia electro-synthesis from nitrogen and water using a cyclic lithium-mediated method |
| Advisors: | Chen, Guohua (ME) Liu, Qiang (ME) |
| Degree: | M.Phil. |
| Year: | 2023 |
| Department: | Department of Mechanical Engineering |
| Pages: | xii, 124 pages : color illustrations |
| Language: | English |
| Abstract: | Ammonia (NH3) synthesis is vital to feed a growing world population. However, its primary synthesizing method, the Haber-Bosch process, is fossil fuels-powered and unsatiable. The lithium-mediated pathway has shown to be a promising alternative to produce ammonia with renewable feedstocks and electric energy. However, its continuous operation is still hampered by limited methods to plate Li stably from its aqueous solution because of its exceptionally high reactivity. In this study, a novel lithium metal battery (LMB)-mimic strategy, consisting of Li+ recovery and Li plating steps, is adapted to electro-plate lithium metals from its aqueous solution. Li+ in the solution is extracted spontaneously by a Li-deficient electrode in the Li recovery step and then electro-plated into metallic Li in a Li-friendly system by the Li plating steps. The obtained Li deposits could be utilized for subsequent nitridation and ammonia synthesis. The LMB-mimic system gave a Li plating efficiency exceeding 95% when the capacity of Li deposits was over 12.65 mAh cm-2. This result was similar to the Faradic efficiency (FE) towards ammonia. After the plating capacity was increased to over 15 mAh cm-2, the FE could reach more than 92 %, which is among the best-reported values. From the experimental results and characterization, the solid-electrolyte interphase (SEI) layer was found to play an essential role in high-efficiency Li plating. During Li plating, a limited amount of Li would be consumed upon its first contact with the electrolyte, forming a protective layer to avoid further consumption. Furthermore, the LMB-mimic system can be operated stably because of the highly reversible phase transition of LiMn2O4 during the Li recovery and plating process. This research provides a stable and efficient method for sustainable ammonia synthesis under ambient pressure. |
| Rights: | All rights reserved |
| Access: | open access |
Copyright Undertaking
As a bona fide Library user, I declare that:
- I will abide by the rules and legal ordinances governing copyright regarding the use of the Database.
- I will use the Database for the purpose of my research or private study only and not for circulation or further reproduction or any other purpose.
- I agree to indemnify and hold the University harmless from and against any loss, damage, cost, liability or expenses arising from copyright infringement or unauthorized usage.
By downloading any item(s) listed above, you acknowledge that you have read and understood the copyright undertaking as stated above, and agree to be bound by all of its terms.
Please use this identifier to cite or link to this item:
https://theses.lib.polyu.edu.hk/handle/200/13670