dc.titleCarbon nanotube microwave-assisted thermal bonding of plastic micro biochipen_US
dcterms.abstractMicrofluidic device has been an emerging field in the past decades. The mounting demand of biochips in the health care area has shifted the manufacturing markets from silicon and glass to polymer. In order to fabricate a plastic biochip, bonding is a critical issue to be addressed to provide a reliable performance. Various bonding methods have been developed such as thermal bonding using low pressure strategy, holed pressure equalizing plates, and hybrid assembly; adhesive bonding using PDMS; solvent bonding using DMSO and methanol; and microwave bonding using a gold thin film. Although there are plenty of methods for plastic chip bonding, thermal bonding is still the preferential method to be used because it can provide a contamination-free homogenous assembly of the final products. Thermal bonding requires heating up of two polymeric substrates to their glass transition state (Tg) and the substrates are sealed under the ultimate contact by applied pressure. However, it always results in an immense energy loss and a microstructural deformation on the bonded biochip, due to the heating of bulky bonding machine and the prolonged waiting time for heat sink during bonding respectively.en_US
dcterms.abstractIn this work, a new thermal bonding method assisted by microwave irradiation with the advantages of material homogeneity, leakage-free and negligible deformation has been developed. Given the promising microwave absorption properties, gold nanoparticles (GNPs) and carbon nanotubes (CNTs) have been used as the microwave absorbers to examine the feasibility on sealing plastic biochips in this study. It was found that CNTs were capable to release tremendous amount of heat energy to seal plastic biochip in an extremely short exposure time of microwave irradiation. The key microstructures on the plastic biochip were the microchannels with dimensions of 50 μm in depth and 100 μm in width. Unlike the previously developed method that CNTs were casted at the bonding interface, they were spray-coated on the non-bonding side of a planar substrate. With this, the bonding interface was homogeneous. The parameters including CNT thickness and exposure time of the proposed bonding method were further optimized to seal the plastic biochips. The microstructures were completely sealed and their integrity was found to be well-maintained through the cross-sectional images observed under microscope. Leakage test was conducted and an injected dye successfully passed through the sealed microchannels without leakage. The bonded biochip was able to withstand a pressure of 2 MPa as found in the tensile test. The bonding method developed in this study possesses the criteria in material homogeneity on bonded assembly, leakage-free on sealing and negligible deformation on prime structures. This bonding method is able to be conducted with short processing time and high bonding efficiency, and to be potentially developed as a high throughput process. CNT-microwave-assisted thermal bonding featuring with these criteria has been developed as a promising alternative for bonding plastic biochips in industrial scale production.en_US
dcterms.extentxvi, 129 p. : ill. ; 30 cm.en_US
dcterms.isPartOfPolyU Electronic Thesesen_US
dcterms.issued2011en_US
dcterms.educationalLevelAll Masteren_US
dcterms.educationalLevelM.Phil.en_US
dcterms.LCSHBiochips.en_US
dcterms.LCSHMicrofluidic devices.en_US
dcterms.LCSHHong Kong Polytechnic University -- Dissertationsen_US
dcterms.accessRightsopen accessen_US

Files in This Item:
File Description SizeFormat 
b25071919.pdfFor All Users4.32 MBAdobe PDFView/Open


Copyright Undertaking

As a bona fide Library user, I declare that:

  1. I will abide by the rules and legal ordinances governing copyright regarding the use of the Database.
  2. I will use the Database for the purpose of my research or private study only and not for circulation or further reproduction or any other purpose.
  3. I agree to indemnify and hold the University harmless from and against any loss, damage, cost, liability or expenses arising from copyright infringement or unauthorized usage.

By downloading any item(s) listed above, you acknowledge that you have read and understood the copyright undertaking as stated above, and agree to be bound by all of its terms.

Show simple item record

Please use this identifier to cite or link to this item: https://theses.lib.polyu.edu.hk/handle/200/6469